Fig. 9: Fracture surfaces of R6 mooring chain steel after SSRT tests in 3.5% NaCl.

a, b at −1150 mV, (c, d) at −1500 mV; (a, c) represent the cracking initiation region for each specimen, while (b, d) correspond to the tensile fracture morphology at the fracture center.