Fig. 1: In situ observation of full dislocation nucleation in a grain that contains both relatively thick and thin twins/matrixes.

a The relatively thick twins/matrixes are free of defects. b Two full dislocations (marked as T) glide on the {111} planes intersecting with the TBs. The scale bars are for 1 nm.