Fig. 3: Dynamic evolution of the diffraction peaks during the laser remelting process. | Nature Communications

Fig. 3: Dynamic evolution of the diffraction peaks during the laser remelting process.

From: In situ observation of crystal rotation in Ni-based superalloy during additive manufacturing process

Fig. 3

a, b The rotation angle (a) and FWHM (b) in the χ direction versus time. c, d The rotation angle (c) and FWHM (d) in the 2θ direction versus time. The red, blue, black and grey dots represent the γ(\(\bar{3}\,\bar{1}\,\bar{1}\)), γ(\(\bar{3}\,\bar{1}\,1\)), γ(1 1 3) and γ(\(1\,1\,\bar{3}\)) lattice planes, respectively. The orange, grey, purple and red rectangular zones denote four different stages of the laser remelting process. The laser was switched on at 150 ms and off at 250 ms.