Fig. 7: The AES spectrum of corrosion film on Mg and Mg-Nd-Zr before and after sputtering respectively in 3.5/10 wt.% NaCl. | npj Materials Degradation

Fig. 7: The AES spectrum of corrosion film on Mg and Mg-Nd-Zr before and after sputtering respectively in 3.5/10 wt.% NaCl.

From: Attain insensitivity to chlorine ions in magnesium alloys by impeding the diffusion process

Fig. 7

a Corrosion film on Mg before/after sputtering in 3.5 wt.% NaCl. b Corrosion film on Mg before/after sputtering in 10 wt.% NaCl. c Corrosion film on Mg-Nd-Zr before/after sputtering in 3.5 wt.% NaCl. d Corrosion film on Mg-Nd-Zr before/after sputtering in 10 wt.% NaCl.