Table 2 Maxima and minima in the scattering anisotropy g for composites with microinclusions of size \({d}_{{g}_{{\rm{\min }}}}\) along with corresponding reflectances \({R}_{{g}_{{\rm{\max }}}}\) and \({R}_{{g}_{{\rm{\min }}}}\) at wavelengths \({\lambda }_{{g}_{{\rm{\max }}}}\) and \({\lambda }_{{g}_{{\rm{\min }}}}\) respectively.
From: Plasmonically Enhanced Reflectance of Heat Radiation from Low-Bandgap Semiconductor Microinclusions
Material | g min | \({{\boldsymbol{d}}}_{{\boldsymbol{g}}{}_{{\bf{\min }}}}\) (μm) | \({{\boldsymbol{\lambda }}}_{{\boldsymbol{g}}{}_{{\bf{\min }}}}\) (μm) | \({{\boldsymbol{R}}}_{{\boldsymbol{g}}{}_{{\bf{\min }}}}\) | g max | \({{\boldsymbol{\lambda }}}_{{\boldsymbol{g}}{}_{{\bf{\max }}}}\) (μm) | \({{\boldsymbol{R}}}_{{\boldsymbol{g}}{}_{{\bf{\max }}}}\) |
|---|---|---|---|---|---|---|---|
InP | −4.94 · 10−2 | 0.60 | 0.96 | 0.76 | 0.547 | 2.16 | 0.71 |
Si | −5.48 · 10−2 | 1.68 | 2.87 | 0.63 | 0.711 | 1.21 | 0.49 |
Ge | −1.19 · 10−1 | 0.64 | 1.56 | 0.71 | 0.524 | 2.98 | 0.72 |
PbS | −1.23 · 10−1 | 1.34 | 3.26 | 0.52 | 0.523 | 6.30 | 0.54 |
InAs | −5.35 · 10−2 | 2.80 | 4.90 | 0.50 | 0.451 | 6.89 | 0.57 |
Te | −2.99 · 10−1 | 1.24 | 3.92 | 0.65 | 0.513 | 7.85 | 0.51 |