Figure 11
From: Centrifugal granulation behavior in metallic powder fabrication by plasma rotating electrode process
(a–c) CtFD-simulated PREP process of Ti64 and (d, e) corresponding PSD fabricated with the end surface morphology of (a) flat plane, (b) shallow depression, and (c) deep depression. Electron diameter was 15 mm; rotating speed was 7000 rpm; melting rate was 7.5 × 10–7 m3/s.
